| ΔH interface M in O (Miedema) |
-556 |
(kJ mol-1) |
|
13823 |
| ΔH interface O in M (Miedema) |
-217 |
(kJ mol-1) |
|
13823 |
| ΔH interface S in M |
0 |
(kJ mol-1) |
|
13823 |
| Δinterface M in S (Miedema) |
0 |
(kJ mol-1) |
|
13823 |
| γ-free electron to specific heat |
0 |
(mJ mol-1 K-2) |
|
13823 |
| Atomic concentration |
7,04 |
(1023 m-3) |
|
13823 |
| Atomic electron scattering factor at 0.5 |
1,99 |
|
|
13823 |
| Atomic environment number (Villars, Daams) |
12 |
|
|
13823 |
| Atomic number start counting left top, left-right sequence |
43 |
|
|
13823 |
| Atomic weight |
98 |
(10-3 kg) |
|
13823 |
| Boiling temperature |
4538 |
(K) |
|
20518 |
| Boiling temperature |
5150 |
(K) |
|
13823 |
| Bulk modulus |
0 |
(GPa) |
|
13823 |
| Charge nuclear effective (Clementi) |
7,23 |
|
|
13823 |
| Chemical potential (Miedema) |
5,3 |
|
|
13823 |
| Compression modulus |
2,97 |
(GPa) |
|
13823 |
| Conductivity electrical |
5,9 |
(104 Ohm-1 cm-1) |
|
13823 |
| Conductivity thermal |
50,6 |
(J mol-1 K-1) |
|
13823 |
| Debye temperature |
453 |
(K) |
|
13823 |
| Density |
11500 |
(kg m-3) |
|
13823 |
| Density |
11000 |
(kg m-3) |
|
20518 |
| Distance to core electron (Schubert) |
0,86 |
(A) |
|
13823 |
| Distance to valence electron (Schubert) |
1,35 |
(A) |
|
13823 |
| Electrochemical weight equivalent |
0,14478 |
(mg K-1) |
|
13823 |
| Electron affinity |
96 |
(kJ mol-1) |
|
13823 |
| Electronegativity (Alfred-Rochow) |
1,36 |
|
|
13823 |
| Electronegativity (Martynov&Batsanov) |
2,18 |
|
|
13823 |
| Electronegativity (Pauling) |
1,9 |
|
|
13823 |
| Electronegativity absolute |
3,91 |
|
|
13823 |
| Energy cohesive (Brewer) |
6,85 |
(J mol-1) |
|
13823 |
| Energy of ionization (first) |
702,4 |
(kJ mol-1) |
|
13823 |
| Energy of ionization (second) |
1472 |
(kJ mol-1) |
|
13823 |
| Energy of ionization (third) |
2850 |
(kJ mol-1) |
|
13823 |
| Enthalpy of atomization |
678 |
(kJ mol-1) |
|
13823 |
| Enthalpy of melting |
23,8 |
(kJ mol-1) |
|
13823 |
| Enthalpy of surface (Miedema) |
186 |
(kJ mol-1) |
|
13823 |
| Enthalpy of vacancies (Miedema) |
195 |
(kJ mol-1) |
|
13823 |
| Enthalpy of vaporization |
585,2 |
(kJ mol-1) |
|
13823 |
| Entropy of solid |
33,4944 |
(J mol-1 K-1) |
|
13823 |
| Group number |
7 |
|
|
13823 |
| Hardness (Brinell) |
0 |
[MPa] |
|
13823 |
| Linear thermal expansion coefficient |
0 |
(10-6 K-1) |
|
13823 |
| Magnetic frequency of nuclei |
22,508 |
|
|
13823 |
| Magnetic resonance |
9,5832 |
(MHz) |
|
13823 |
| Magnetic susceptibility |
0,000000031 |
(m3 kg-1) |
|
13823 |
| Mass attenuation coefficient FeKα |
316 |
(cm2 g-1) |
|
13823 |
| Mass attenuation coefficient for CrKα |
485 |
(cm2 g-1) |
|
13823 |
| Mass attenuation coefficient for CuKα |
172 |
(cm2 g-1) |
|
13823 |
| Mass attenuation coefficient for MoKα |
19,7 |
(cm2 g-1) |
|
13823 |
| Melting temperature |
2445 |
(K) |
|
13823 |
| Melting temperature |
2430 |
(K) |
|
20518 |
| Mendeleev chemists sequence |
65 |
|
|
13823 |
| Mendeleev d-t start left |
56 |
|
|
13823 |
| Mendeleev d-t start right |
48 |
|
|
13823 |
| Mendeleev H d-t start left |
55 |
|
|
13823 |
| Mendeleev H d-t start right |
49 |
|
|
13823 |
| Mendeleev H t-d start left |
55 |
|
|
13823 |
| Mendeleev H t-d start right |
49 |
|
|
13823 |
| Mendeleev Pettifor |
59 |
|
|
13823 |
| Mendeleev Pettifor regular |
59 |
|
|
13823 |
| Mendeleev t-d start left |
56 |
|
|
13823 |
| Mendeleev t-d start right |
48 |
|
|
13823 |
| Modulus of rigidity |
0 |
(GPa) |
|
13823 |
| Molar heat capacity |
25,88 |
(J mol-1 K-1) |
|
13823 |
| Moment nuclear magnetic |
1 |
(mu) |
|
13823 |
| Nuclear charge effective (Slater) |
3,6 |
|
|
13823 |
| nWS^(1/3) (Miedema) |
1,81 |
(a.u.-1/3) |
|
13823 |
| Oxidation state (first) |
4 |
|
|
13823 |
| Periodic number start counting bottom right, right-left sequence |
61 |
|
|
13823 |
| Periodic number start counting left bottom, left-right sequence |
56 |
|
|
13823 |
| Periodic number start counting top right, right-left sequence |
48 |
|
|
13823 |
| Poisson's ratio |
0 |
|
|
13823 |
| Quantum number |
5 |
|
|
13823 |
| Radii covalent |
127 |
(pm) |
|
13823 |
| Radii metal (Waber) |
1,36 |
(A) |
|
13823 |
| Radii pseudo-potential (Zunger) |
2,65 |
|
|
13823 |
| Resistivity electrical |
22,6 |
(10-8 Ohm m) |
|
13823 |
| Sound velocity |
0 |
(m s-1) |
|
13823 |
| Spectral lines no |
100 |
|
|
13823 |
| Spin nuclei |
2,5 |
(h) |
|
13823 |
| Surface tension at Tm |
3150 |
(mJ m-2) |
|
13823 |
| Thermal neutron capture cross section |
22 |
(barns) |
|
13823 |
| V^(2/3) (Miedema) |
4,21 |
(cm2) |
|
13823 |
| Valence electron number |
7 |
|
|
13823 |
| Vapour pressure at Tm |
0,0229 |
(N m-2) |
|
13823 |
| Volume of atom (Villars, Daams) |
1,43 |
(10-2 nm3) |
|
13823 |
| Work function |
0 |
(eV) |
|
13823 |
| Young's modulus |
0 |
(GPa) |
|
13823 |