| ΔH interface M in O (Miedema) |
-972 |
(kJ mol-1) |
|
13823 |
| ΔH interface O in M (Miedema) |
-621 |
(kJ mol-1) |
|
13823 |
| ΔH interface S in M |
0 |
(kJ mol-1) |
|
13823 |
| Δinterface M in S (Miedema) |
0 |
(kJ mol-1) |
|
13823 |
| γ-free electron to specific heat |
0 |
(mJ mol-1 K-2) |
|
13823 |
| Atomic concentration |
3,22 |
(1023 m-3) |
|
13823 |
| Atomic electron scattering factor at 0.5 |
2,74 |
|
|
13823 |
| Atomic environment number (Villars, Daams) |
12 |
|
|
13823 |
| Atomic number start counting left top, left-right sequence |
65 |
|
|
13823 |
| Atomic weight |
158,925 |
(10-3 kg) |
|
13823 |
| Boiling temperature |
3467 |
(K) |
|
5391 |
| Boiling temperature |
3396 |
(K) |
|
13823 |
| Boiling temperature |
3073 |
(K) |
|
19178 |
| Boiling temperature |
3493 |
(K) |
|
19178 |
| Boiling temperature |
3503 |
(K) |
|
19178 |
| Bulk modulus |
38,7 |
(GPa) |
|
13823 |
| Charge nuclear effective (Clementi) |
8,3 |
|
|
13823 |
| Chemical potential (Miedema) |
3,21 |
|
|
13823 |
| Compression modulus |
0,399 |
(GPa) |
|
13823 |
| Conductivity electrical |
0,86 |
(104 Ohm-1 cm-1) |
|
13823 |
| Conductivity thermal |
11,1 |
(J mol-1 K-1) |
|
13823 |
| Debye temperature |
169,6 |
(K) |
|
20518 |
| Density |
8229 |
(kg m-3) |
|
13823 |
| Density |
8219 |
(kg m-3) |
orthorhombic, 220 K |
20518 |
| Density |
8230 |
(kg m-3) |
hcp, 297 K |
20518 |
| Density |
7820 |
(kg m-3) |
bcc, 1562 K |
20518 |
| Distance to core electron (Schubert) |
1,08 |
(A) |
|
13823 |
| Distance to valence electron (Schubert) |
2,2 |
(A) |
|
13823 |
| Electrochemical weight equivalent |
0,54991 |
(mg K-1) |
|
13823 |
| Electron affinity |
50 |
(kJ mol-1) |
|
13823 |
| Electronegativity (Alfred-Rochow) |
1,1 |
|
|
13823 |
| Electronegativity (Martynov&Batsanov) |
1,2 |
|
|
13823 |
| Electronegativity (Pauling) |
1,1 |
|
|
13823 |
| Electronegativity absolute |
3,2 |
|
|
13823 |
| Energy cohesive (Brewer) |
4,05 |
(J mol-1) |
|
13823 |
| Energy of ionization (first) |
564,4 |
(kJ mol-1) |
|
13823 |
| Energy of ionization (second) |
1112 |
(kJ mol-1) |
|
13823 |
| Energy of ionization (third) |
2122 |
(kJ mol-1) |
|
13823 |
| Enthalpy of atomization |
388,7 |
(kJ mol-1) |
|
13823 |
| Enthalpy of atomization |
386,5 |
(kJ mol-1) |
|
5391 |
| Enthalpy of melting |
10,86 |
(kJ mol-1) |
|
18453 |
| Enthalpy of melting |
10,193 |
(kJ mol-1) |
|
5391 |
| Enthalpy of melting |
16,3 |
(kJ mol-1) |
|
13823 |
| Enthalpy of surface (Miedema) |
115 |
(kJ mol-1) |
|
13823 |
| Enthalpy of vacancies (Miedema) |
120 |
(kJ mol-1) |
|
13823 |
| Enthalpy of vaporization |
293 |
(kJ mol-1) |
|
19178 |
| Enthalpy of vaporization |
391 |
(kJ mol-1) |
|
13823 |
| Entropy of solid |
73,38 |
(J mol-1 K-1) |
|
5391 |
| Entropy of solid |
72,24 |
(J mol-1 K-1) |
|
18453 |
| Entropy of solid |
73,10153 |
(J mol-1 K-1) |
|
13823 |
| Group number |
3 |
|
|
13823 |
| Hardness (Brinell) |
874 |
[MPa] |
|
13823 |
| Linear thermal expansion coefficient |
9,5 |
(10-6 K-1) |
|
13823 |
| Linear thermal expansion coefficient |
10,3 |
(10-6 K-1) |
|
20518 |
| Magnetic frequency of nuclei |
22,678 |
|
|
13823 |
| Magnetic resonance |
9,7 |
(MHz) |
|
13823 |
| Magnetic susceptibility |
0,0000115 |
(m3 kg-1) |
|
13823 |
| Mass attenuation coefficient FeKα |
214 |
(cm2 g-1) |
|
13823 |
| Mass attenuation coefficient for CrKα |
329 |
(cm2 g-1) |
|
13823 |
| Mass attenuation coefficient for CuKα |
273 |
(cm2 g-1) |
|
13823 |
| Mass attenuation coefficient for MoKα |
67,5 |
(cm2 g-1) |
|
13823 |
| Melting temperature |
1627 |
(K) |
|
18453 |
| Melting temperature |
1629 |
(K) |
|
5391 |
| Melting temperature |
1633 |
(K) |
|
13823 |
| Mendeleev chemists sequence |
41 |
|
|
13823 |
| Mendeleev d-t start left |
33 |
|
|
13823 |
| Mendeleev d-t start right |
72 |
|
|
13823 |
| Mendeleev H d-t start left |
32 |
|
|
13823 |
| Mendeleev H d-t start right |
73 |
|
|
13823 |
| Mendeleev H t-d start left |
31 |
|
|
13823 |
| Mendeleev H t-d start right |
72 |
|
|
13823 |
| Mendeleev Pettifor |
26 |
|
|
13823 |
| Mendeleev Pettifor regular |
26 |
|
|
13823 |
| Mendeleev t-d start left |
32 |
|
|
13823 |
| Mendeleev t-d start right |
71 |
|
|
13823 |
| Modulus of rigidity |
22,1 |
(GPa) |
|
13823 |
| Molar heat capacity |
27,718 |
(J mol-1 K-1) |
|
18453 |
| Molar heat capacity |
28,91 |
(J mol-1 K-1) |
|
13823 |
| Molar heat capacity |
28,95 |
(J mol-1 K-1) |
|
5391 |
| Moment nuclear magnetic |
1,52 |
(mu) |
|
13823 |
| Nuclear charge effective (Slater) |
2,85 |
|
|
13823 |
| nWS^(1/3) (Miedema) |
1,22 |
(a.u.-1/3) |
|
13823 |
| Oxidation state (first) |
3 |
|
|
13823 |
| Periodic number start counting bottom right, right-left sequence |
39 |
|
|
13823 |
| Periodic number start counting left bottom, left-right sequence |
28 |
|
|
13823 |
| Periodic number start counting top right, right-left sequence |
76 |
|
|
13823 |
| Poisson's ratio |
0,261 |
|
|
13823 |
| Quantum number |
6 |
|
|
13823 |
| Radii covalent |
159 |
(pm) |
|
13823 |
| Radii metal (Waber) |
1,782 |
(A) |
|
13823 |
| Radii pseudo-potential (Zunger) |
3,89 |
|
|
13823 |
| Resistivity electrical |
114 |
(10-8 Ohm m) |
|
13823 |
| Sound velocity |
2620 |
(m s-1) |
|
13823 |
| Spectral lines no |
129 |
|
|
13823 |
| Spin nuclei |
1,5 |
(h) |
|
13823 |
| Surface tension at Tm |
1130 |
(mJ m-2) |
|
13823 |
| Thermal neutron capture cross section |
23 |
(barns) |
|
13823 |
| V^(2/3) (Miedema) |
7,2 |
(cm2) |
|
13823 |
| Valence electron number |
3 |
|
|
13823 |
| Vapour pressure at Tm |
0 |
(N m-2) |
|
13823 |
| Volume of atom (Villars, Daams) |
3,213 |
(10-2 nm3) |
|
13823 |
| Work function |
3,1 |
(eV) |
|
13823 |
| Young's modulus |
55,7 |
(GPa) |
|
13823 |